Subgroup

Tests /Conditions

SS 

Accept #

Subgroup 1

a.  Physical Dimensions - Mil-Std-883 Method 2016

15

0 reject

Subgroup 2

a.  Lead Integrity - Mil-Std-883 Method 2004

      - test condition B2 (Lead Fatigue)

45

0 reject

b.  Seal Integrity - Mil-Std-883 Method 1014

1)  Fine Leak Test

2) Gross Leak Test

45

0 reject

Subgroup 3

a.  Thermal Shock - Mil-Std-883 Method 1011

- test condition B min.; 15X min.

15

0 reject

b. Temperature Cycle - Mil-Std-883 Method 1010

- test condition C, 100X min.

15

0 reject

c.  Moisture Resistance - Mil-Std-883 Method 1004

15

0 reject

d. Visual Inspection - per criteria in Mil-Std-883 Methods 1004 and 1010

15

0 reject

e.  Seal Integrity - Mil-Std-883 Method 1014

1)  Fine Leak Test

2) Gross Leak Test

15

0 reject

f.  End-point electrical parameters

- Per the applicable device specifications

15

0 reject

Subgroup 4

a.  Mechanical Shock - Mil-Std-883 Method 2002

- test condition B min.

15

0 reject

b. Vibration Test, Variable Frequency - Mil-Std-883 Method 2007

- test condition A min.

15

0 reject

c.  Constant Acceleration - Mil-Std-883 Method

2001

- test condition E min.

15

0 reject

d. Seal Integrity - Mil-Std-883 Method 1014

1)  Fine Leak Test

2) Gross Leak Test

15

0 reject

e. Visual Inspection - per criteria in Mil-Std-883 Methods 1010 or 1011

15

0 reject

f.  End-point electrical parameters

- Per the applicable device specifications

15

0 reject

Subgroup 5

a.  Salt Atmosphere Test - Mil-Std-883 Method 1009

15

0 reject

b. Visual Inspection - per criteria in Mil-Std-883 Method 1009

15

0 reject

c.  Seal Integrity - Mil-Std-883 Method 1014

1)  Fine Leak Test

2) Gross Leak Test

15

0 reject

Subgroup 6

a.  Internal Water Vapor Content - Mil-Std-883 Method 1018

- 5,000 ppm max water content at 100C

3 (or 5)

0 reject for SS=3;

1 reject for SS=5

Subgroup 7

a.  Adhesion of Lead Finish - Mil-Std-883 Method 2025

15

0 reject

Subgroup 8

a.  Lid Torque Test - Mil-Std-883 Method 2024

5

0 reject